Influence of HSS drill coatings on surface finish and cylindricity of AA6061/C/ZrO2 composite in CNC drilling operations under dry conditions

This study aims to evaluate the effect of HSS drill tool coatings, namely single-layer TiN, single-layer AlCrN, and double-layer AlTiN + TiSiXN (Durana), on the surface roughness and cylindricity of AA6061 (90 wt%)/C (5 wt%)/ZrO2 (5 wt%) hybrid composite material processed by the stir casting method. The fabricated sample was examined for the uniform particle distribution of reinforcements using Scanning Electron Microscope. The drilling operation was carried out on the fabricated in a CNC machining center by setting the spindle speeds of 800, 1200, and 1600 rpm, depths of cut of 0.5, 1, and 1.5 mm, and feeds of 50, 100, and 150 mm/rev. An orthogonal array (L27) designed by Taguchi’s method was used as the design of the experiment for the optimization of the best cutting parameters and coating. Surface roughness and cylindricity errors were determined for the 27 experimental runs. Field emission scanning electron microscopic (FESEM) examination and Energy Dispersive Spectroscopy (EDS) were used to analyze the surface integrity and elemental composition, respectively. The results revealed that Durana had a significant effect on the surface substrate with minimum surface roughness (Ra) of 1.666 μm and obtained the minimum cylindricity error for the parameters of depth of cut 0.5 mm, spindle speed of 1200 and feed of 100 mm rev−1.