Selectivity Study of Direct Seawater Electrolyzer Anode Catalysts Using the Rotating Ring-Disc Electrode Method

Seawater electrolysis suffers from many issues that must be resolved before the technology can be scaled. The corrosive hypochlorite formation at the anode can damage the electrode and other electrolyzer components. Furthermore, hypochlorite is unstable and can decay, particularly when exposed to heat and metal ions, which could lead to erroneously high oxygen evolution reaction (OER) selectivity calculations in catalyst benchmarking experiments, resulting in poor catalyst and electrolyzer component selection. In this study, we used the rotating ring-disc electrode (RRDE) technique for the characterization of IrO₂, NiO, Co₃O₄, RuO₂, Pt/C, and PtRu electrocatalysts at near-neutral pH (8.4) in 0.5 M NaCl. The RRDE can overcome the challenge posed by thermocatalytic hypochlorite decay. IrO₂ and PtRu were also studied over a range of chloride concentrations from 0.1 to 1 M. Our findings reveal that elevated temperatures (313 and 333 K) are conducive to higher OER selectivity, as the OER faradaic efficiency (FE) on IrO₂ increased by 23% at 1.22 V vs SHE when the temperature was increased from 293 to 333 K. Increasing the chloride concentration from 0.1 to 1 M increased the OER current density by 40% and 200% on IrO₂ and PtRu, respectively, indicating a synergistic relationship.