Yupeng Miao , Chunlei Gan , Ming Wang , Lozikov Igor
{"title":"不同时效状态下 Cu-Cr-Zr-Nb 合金的相结构、硬度和磨损性能","authors":"Yupeng Miao , Chunlei Gan , Ming Wang , Lozikov Igor","doi":"10.1016/j.jmrt.2024.09.073","DOIUrl":null,"url":null,"abstract":"<div><p>As a typical age-strengthened alloy, Cu–Cr–Zr alloys have high strength, good electrical conductivity, and excellent wear resistance. In this work, the Cu–Cr–Zr–Nb alloys were in different aging states after the aging process. After aging at 460 °C for 4 h, the alloy was peak-aging. The common effect of the existence of the FCC Cr particle, which was coherent with the Cu matrix, and the increase in hardness improved the wear property of the alloy. The results of the wear test showed that the optimal wear parameter was a speed of 300 rpm and a load of 5 N. Under these wear parameters, the alloy had the lowest mean coefficient of friction (COF) value and the least mass loss, having the best wear resistance. Furthermore, the wear mechanism of the alloy was mainly adhesive wear and abrasive wear.</p></div>","PeriodicalId":54332,"journal":{"name":"Journal of Materials Research and Technology-Jmr&t","volume":"33 ","pages":"Pages 515-525"},"PeriodicalIF":6.2000,"publicationDate":"2024-09-13","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://www.sciencedirect.com/science/article/pii/S2238785424020787/pdfft?md5=37f7378356792fbfa2dac39c10e3a433&pid=1-s2.0-S2238785424020787-main.pdf","citationCount":"0","resultStr":"{\"title\":\"The phase structure, hardness, and wear properties of the Cu–Cr–Zr–Nb alloy under different aging states\",\"authors\":\"Yupeng Miao , Chunlei Gan , Ming Wang , Lozikov Igor\",\"doi\":\"10.1016/j.jmrt.2024.09.073\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><p>As a typical age-strengthened alloy, Cu–Cr–Zr alloys have high strength, good electrical conductivity, and excellent wear resistance. In this work, the Cu–Cr–Zr–Nb alloys were in different aging states after the aging process. After aging at 460 °C for 4 h, the alloy was peak-aging. The common effect of the existence of the FCC Cr particle, which was coherent with the Cu matrix, and the increase in hardness improved the wear property of the alloy. The results of the wear test showed that the optimal wear parameter was a speed of 300 rpm and a load of 5 N. Under these wear parameters, the alloy had the lowest mean coefficient of friction (COF) value and the least mass loss, having the best wear resistance. Furthermore, the wear mechanism of the alloy was mainly adhesive wear and abrasive wear.</p></div>\",\"PeriodicalId\":54332,\"journal\":{\"name\":\"Journal of Materials Research and Technology-Jmr&t\",\"volume\":\"33 \",\"pages\":\"Pages 515-525\"},\"PeriodicalIF\":6.2000,\"publicationDate\":\"2024-09-13\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"https://www.sciencedirect.com/science/article/pii/S2238785424020787/pdfft?md5=37f7378356792fbfa2dac39c10e3a433&pid=1-s2.0-S2238785424020787-main.pdf\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Journal of Materials Research and Technology-Jmr&t\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://www.sciencedirect.com/science/article/pii/S2238785424020787\",\"RegionNum\":2,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q1\",\"JCRName\":\"MATERIALS SCIENCE, MULTIDISCIPLINARY\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Journal of Materials Research and Technology-Jmr&t","FirstCategoryId":"88","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S2238785424020787","RegionNum":2,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
The phase structure, hardness, and wear properties of the Cu–Cr–Zr–Nb alloy under different aging states
As a typical age-strengthened alloy, Cu–Cr–Zr alloys have high strength, good electrical conductivity, and excellent wear resistance. In this work, the Cu–Cr–Zr–Nb alloys were in different aging states after the aging process. After aging at 460 °C for 4 h, the alloy was peak-aging. The common effect of the existence of the FCC Cr particle, which was coherent with the Cu matrix, and the increase in hardness improved the wear property of the alloy. The results of the wear test showed that the optimal wear parameter was a speed of 300 rpm and a load of 5 N. Under these wear parameters, the alloy had the lowest mean coefficient of friction (COF) value and the least mass loss, having the best wear resistance. Furthermore, the wear mechanism of the alloy was mainly adhesive wear and abrasive wear.
期刊介绍:
The Journal of Materials Research and Technology is a publication of ABM - Brazilian Metallurgical, Materials and Mining Association - and publishes four issues per year also with a free version online (www.jmrt.com.br). The journal provides an international medium for the publication of theoretical and experimental studies related to Metallurgy, Materials and Minerals research and technology. Appropriate submissions to the Journal of Materials Research and Technology should include scientific and/or engineering factors which affect processes and products in the Metallurgy, Materials and Mining areas.