{"title":"氧化鳞对 SUS301L 不锈钢焊接接头耐腐蚀性的影响","authors":"","doi":"10.1016/j.matchar.2024.114431","DOIUrl":null,"url":null,"abstract":"<div><div>The effect of thermal oxidates on the corrosion of SUS301L stainless steel welded joint was investigated using electrochemical corrosion test and TEM microstructure observation. Activation dissolution behavior without passive region was found in the potentiodynamic polarization curves on the welding zone and heat affected zone. The activation corrosion is related to the preferential dissolution of the Ni<img>Fe layer at the interface between chromium oxide and substrate. However, the passive region in the polarization curve reappears after the unstable Ni<img>Fe dissolves in the salt-frog test. The passivation behavior due to microstructure evolution beneath the thermal oxide film was discussed during the corrosion process.</div></div>","PeriodicalId":18727,"journal":{"name":"Materials Characterization","volume":null,"pages":null},"PeriodicalIF":4.8000,"publicationDate":"2024-10-02","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":"0","resultStr":"{\"title\":\"The effect of oxide scale on the corrosion resistance of SUS301L stainless steel welding joints\",\"authors\":\"\",\"doi\":\"10.1016/j.matchar.2024.114431\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"<div><div>The effect of thermal oxidates on the corrosion of SUS301L stainless steel welded joint was investigated using electrochemical corrosion test and TEM microstructure observation. Activation dissolution behavior without passive region was found in the potentiodynamic polarization curves on the welding zone and heat affected zone. The activation corrosion is related to the preferential dissolution of the Ni<img>Fe layer at the interface between chromium oxide and substrate. However, the passive region in the polarization curve reappears after the unstable Ni<img>Fe dissolves in the salt-frog test. The passivation behavior due to microstructure evolution beneath the thermal oxide film was discussed during the corrosion process.</div></div>\",\"PeriodicalId\":18727,\"journal\":{\"name\":\"Materials Characterization\",\"volume\":null,\"pages\":null},\"PeriodicalIF\":4.8000,\"publicationDate\":\"2024-10-02\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"Materials Characterization\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://www.sciencedirect.com/science/article/pii/S104458032400812X\",\"RegionNum\":2,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q1\",\"JCRName\":\"MATERIALS SCIENCE, CHARACTERIZATION & TESTING\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"Materials Characterization","FirstCategoryId":"88","ListUrlMain":"https://www.sciencedirect.com/science/article/pii/S104458032400812X","RegionNum":2,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"MATERIALS SCIENCE, CHARACTERIZATION & TESTING","Score":null,"Total":0}
引用次数: 0
摘要
利用电化学腐蚀试验和 TEM 显微结构观察研究了热氧化物对 SUS301L 不锈钢焊接接头腐蚀的影响。在焊接区和热影响区的电位极化曲线中发现了无被动区的活化溶解行为。活化腐蚀与氧化铬和基体界面上的镍铁合金层优先溶解有关。然而，在盐蛙试验中，不稳定的镍铁层溶解后，极化曲线中的被动区再次出现。在腐蚀过程中，讨论了热氧化膜下微观结构演变导致的钝化行为。
The effect of oxide scale on the corrosion resistance of SUS301L stainless steel welding joints
The effect of thermal oxidates on the corrosion of SUS301L stainless steel welded joint was investigated using electrochemical corrosion test and TEM microstructure observation. Activation dissolution behavior without passive region was found in the potentiodynamic polarization curves on the welding zone and heat affected zone. The activation corrosion is related to the preferential dissolution of the NiFe layer at the interface between chromium oxide and substrate. However, the passive region in the polarization curve reappears after the unstable NiFe dissolves in the salt-frog test. The passivation behavior due to microstructure evolution beneath the thermal oxide film was discussed during the corrosion process.
期刊介绍：
Materials Characterization features original articles and state-of-the-art reviews on theoretical and practical aspects of the structure and behaviour of materials.
The Journal focuses on all characterization techniques, including all forms of microscopy (light, electron, acoustic, etc.,) and analysis (especially microanalysis and surface analytical techniques). Developments in both this wide range of techniques and their application to the quantification of the microstructure of materials are essential facets of the Journal.
The Journal provides the Materials Scientist/Engineer with up-to-date information on many types of materials with an underlying theme of explaining the behavior of materials using novel approaches. Materials covered by the journal include:
Metals & Alloys
Ceramics
Nanomaterials
Biomedical materials
Optical materials
Composites
Natural Materials.
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们