{"title":"湿度变化对表面盐沉积 AA7085-T7451 腐蚀疲劳的影响","authors":"Brandon Free, Gabriella C. Montiel, Gabriella A. Marino, Eric Schindelholz, Sarah Galyon Dorman, Jenifer S. Warner Locke","doi":"10.1038/s41529-024-00530-1","DOIUrl":null,"url":null,"abstract":"Corrosion fatigue (CF) crack growth is quantified as a function of relative humidity (RH) using AA7085-T7451 samples with NaCl deposited to understand the effect of deliquesced surface electrolyte droplets on CF performance when humidity varies. Fracture mechanics testing holding mechanical driving forces for cracking constant and incrementally increasing humidity show that crack growth rate (da/dN) more than doubles once RH moves above 78–80% RH. When decreasing RH, some amount of drying below the efflorescence RH (ERH) and/or a sufficient time is needed to pass in order for da/dN to return to that expected for a dry crack tip. All in all, this study establishes time of crack tip wetness as an important parameter for predicting fatigue lifetimes in atmospheric conditions, a parameter that cannot be solely predicted by RH, as accelerated cracking can continue for a limited amount of time even when RH is brought below the ERH.","PeriodicalId":19270,"journal":{"name":"npj Materials Degradation","volume":" ","pages":"1-12"},"PeriodicalIF":6.6000,"publicationDate":"2024-11-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"https://www.nature.com/articles/s41529-024-00530-1.pdf","citationCount":"0","resultStr":"{\"title\":\"The effect of variable humidity on corrosion fatigue of AA7085-T7451 with surface salt deposits\",\"authors\":\"Brandon Free, Gabriella C. Montiel, Gabriella A. Marino, Eric Schindelholz, Sarah Galyon Dorman, Jenifer S. Warner Locke\",\"doi\":\"10.1038/s41529-024-00530-1\",\"DOIUrl\":null,\"url\":null,\"abstract\":\"Corrosion fatigue (CF) crack growth is quantified as a function of relative humidity (RH) using AA7085-T7451 samples with NaCl deposited to understand the effect of deliquesced surface electrolyte droplets on CF performance when humidity varies. Fracture mechanics testing holding mechanical driving forces for cracking constant and incrementally increasing humidity show that crack growth rate (da/dN) more than doubles once RH moves above 78–80% RH. When decreasing RH, some amount of drying below the efflorescence RH (ERH) and/or a sufficient time is needed to pass in order for da/dN to return to that expected for a dry crack tip. All in all, this study establishes time of crack tip wetness as an important parameter for predicting fatigue lifetimes in atmospheric conditions, a parameter that cannot be solely predicted by RH, as accelerated cracking can continue for a limited amount of time even when RH is brought below the ERH.\",\"PeriodicalId\":19270,\"journal\":{\"name\":\"npj Materials Degradation\",\"volume\":\" \",\"pages\":\"1-12\"},\"PeriodicalIF\":6.6000,\"publicationDate\":\"2024-11-01\",\"publicationTypes\":\"Journal Article\",\"fieldsOfStudy\":null,\"isOpenAccess\":false,\"openAccessPdf\":\"https://www.nature.com/articles/s41529-024-00530-1.pdf\",\"citationCount\":\"0\",\"resultStr\":null,\"platform\":\"Semanticscholar\",\"paperid\":null,\"PeriodicalName\":\"npj Materials Degradation\",\"FirstCategoryId\":\"88\",\"ListUrlMain\":\"https://www.nature.com/articles/s41529-024-00530-1\",\"RegionNum\":2,\"RegionCategory\":\"材料科学\",\"ArticlePicture\":[],\"TitleCN\":null,\"AbstractTextCN\":null,\"PMCID\":null,\"EPubDate\":\"\",\"PubModel\":\"\",\"JCR\":\"Q1\",\"JCRName\":\"MATERIALS SCIENCE, MULTIDISCIPLINARY\",\"Score\":null,\"Total\":0}","platform":"Semanticscholar","paperid":null,"PeriodicalName":"npj Materials Degradation","FirstCategoryId":"88","ListUrlMain":"https://www.nature.com/articles/s41529-024-00530-1","RegionNum":2,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":null,"EPubDate":"","PubModel":"","JCR":"Q1","JCRName":"MATERIALS SCIENCE, MULTIDISCIPLINARY","Score":null,"Total":0}
The effect of variable humidity on corrosion fatigue of AA7085-T7451 with surface salt deposits
Corrosion fatigue (CF) crack growth is quantified as a function of relative humidity (RH) using AA7085-T7451 samples with NaCl deposited to understand the effect of deliquesced surface electrolyte droplets on CF performance when humidity varies. Fracture mechanics testing holding mechanical driving forces for cracking constant and incrementally increasing humidity show that crack growth rate (da/dN) more than doubles once RH moves above 78–80% RH. When decreasing RH, some amount of drying below the efflorescence RH (ERH) and/or a sufficient time is needed to pass in order for da/dN to return to that expected for a dry crack tip. All in all, this study establishes time of crack tip wetness as an important parameter for predicting fatigue lifetimes in atmospheric conditions, a parameter that cannot be solely predicted by RH, as accelerated cracking can continue for a limited amount of time even when RH is brought below the ERH.
期刊介绍：
npj Materials Degradation considers basic and applied research that explores all aspects of the degradation of metallic and non-metallic materials. The journal broadly defines ‘materials degradation’ as a reduction in the ability of a material to perform its task in-service as a result of environmental exposure.
The journal covers a broad range of topics including but not limited to:
-Degradation of metals, glasses, minerals, polymers, ceramics, cements and composites in natural and engineered environments, as a result of various stimuli
-Computational and experimental studies of degradation mechanisms and kinetics
-Characterization of degradation by traditional and emerging techniques
-New approaches and technologies for enhancing resistance to degradation
-Inspection and monitoring techniques for materials in-service, such as sensing technologies
京公网安备 11010802042870号
京ICP备2023020795号-1
分享
求助内容：
应助结果提醒方式：
扫码关注我们