Manufacturing of High Purity Cr2AlC MAX Phase Material and Its Characterization

Present study discusses about a technique for producing high-purity Cr₂AlC MAX phase materials and gaining insight into their thermal behavior for high-temperature applications. The research conducted involved synthesizing a pure layered ternary carbide Cr₂AlC MAX phase material by mixing powders of Chromium, Aluminum, and Carbon and then subjecting them to two-step pressureless sintering process in argon atmosphere. First step involves the annealing of ball-milled mixture at 750 °C for 2 h followed by the second step in which the annealed mixture is subjected to heat-treatment at 1350 °C for 2 h. Analysis using XRD and Raman techniques revealed that the synthesized product consists of Cr₂AlC phase, without any impurities. SEM studies confirmed that the Cr₂AlC had a layered topography, while EPMA analysis indicated that the atomic percentage of Cr, Al, and C was consistent with the XRD phase analysis. XPS investigations confirmed the presence of Cr-C bonds representing M_n+1X_n of the MAX phase material. TG-DSC results showed an approximately 2% increase in weight. The Cr₂AlC phase exhibited an endothermic pattern below 725 °C, an exothermic pattern above it, and did not decompose up to 1400 °C in vacuum environment. High-temperature XRD analysis at various temperatures also confirmed no formation of Al₂O₃ or CrO impurity compounds.