Pub Date : 2023-01-01DOI: 10.32604/jrm.2023.031129
Arnoldo E. Alfaro-Corres, D. González-Mendoza, E. Ruiz-Sánchez, Carlos Ail-Catzin, B. Valdez-Salas, F. Gutiérrez-Miceli, A. Reyes-Ramírez, Jacques Fils
This work was carried out to evaluate the insecticidal effect of mono, bi and trimetallic nanoparticles (NPs) from leaf extract of habanero pepper ( Capsicum chinense Jacq.) on the red fl our beetle ( Tribolium castaneum herbst.) and cotton mealybug ( Phenacoccus solenopsis Tinsley). The results showed that Cu NPs, Cu/Mn NPs and Zn/Cu NPs had high insecticidal effect against T. castaneum (63% – 80% mortality after 96 h). The Cu NPs and Zn/Cu NPs showed also insecticidal effect against P. solenopsis , but to a lesser extent (20% – 28% after 96 h). With regards to the physicochemical characterization, Cu NPs had a zeta potential of 21.1 mV, whereas Cu/Mn NPs and Zn/Cu NPs exhibited zeta potentials of 200 mV. The polydispersity index (PDI) values for Cu NPs, Cu/Mn NPs, and Zn/ Cu NPs were 10.1, 29.16, and 14.34, respectively. The TF-IR spectra of the NPs varied from 600 to 4000 cm − 1 . The EDX weight percentages showed the presence of Cu (0.29% – 2.4%), Mn (1.4%), and Zn (2.6%) in Cu/Mn NPs and Zn/Cu NPs, respectively.
{"title":"Insecticidal Activity and Physicochemical Characterization of Nanoparticles from Foliar Extract of Capsicum chinense","authors":"Arnoldo E. Alfaro-Corres, D. González-Mendoza, E. Ruiz-Sánchez, Carlos Ail-Catzin, B. Valdez-Salas, F. Gutiérrez-Miceli, A. Reyes-Ramírez, Jacques Fils","doi":"10.32604/jrm.2023.031129","DOIUrl":"https://doi.org/10.32604/jrm.2023.031129","url":null,"abstract":"This work was carried out to evaluate the insecticidal effect of mono, bi and trimetallic nanoparticles (NPs) from leaf extract of habanero pepper ( Capsicum chinense Jacq.) on the red fl our beetle ( Tribolium castaneum herbst.) and cotton mealybug ( Phenacoccus solenopsis Tinsley). The results showed that Cu NPs, Cu/Mn NPs and Zn/Cu NPs had high insecticidal effect against T. castaneum (63% – 80% mortality after 96 h). The Cu NPs and Zn/Cu NPs showed also insecticidal effect against P. solenopsis , but to a lesser extent (20% – 28% after 96 h). With regards to the physicochemical characterization, Cu NPs had a zeta potential of 21.1 mV, whereas Cu/Mn NPs and Zn/Cu NPs exhibited zeta potentials of 200 mV. The polydispersity index (PDI) values for Cu NPs, Cu/Mn NPs, and Zn/ Cu NPs were 10.1, 29.16, and 14.34, respectively. The TF-IR spectra of the NPs varied from 600 to 4000 cm − 1 . The EDX weight percentages showed the presence of Cu (0.29% – 2.4%), Mn (1.4%), and Zn (2.6%) in Cu/Mn NPs and Zn/Cu NPs, respectively.","PeriodicalId":16952,"journal":{"name":"Journal of Renewable Materials","volume":null,"pages":null},"PeriodicalIF":0.0,"publicationDate":"2023-01-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":null,"resultStr":null,"platform":"Semanticscholar","paperid":"69860901","PeriodicalName":null,"FirstCategoryId":null,"ListUrlMain":null,"RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":"","EPubDate":null,"PubModel":null,"JCR":null,"JCRName":null,"Score":null,"Total":0}
{"title":"Design and Development of Composite Plywood that Integrates Fire Resistance, Water Resistance and Wear Resistance","authors":"X. Liang, Xiaoyu Gu, Myint Myint Paing Hsu, Yuhang He, Rongzhuo Zhang, Conghui Cai, Zheng Wang","doi":"10.32604/jrm.2023.026137","DOIUrl":"https://doi.org/10.32604/jrm.2023.026137","url":null,"abstract":"","PeriodicalId":16952,"journal":{"name":"Journal of Renewable Materials","volume":null,"pages":null},"PeriodicalIF":0.0,"publicationDate":"2023-01-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":null,"resultStr":null,"platform":"Semanticscholar","paperid":"69853632","PeriodicalName":null,"FirstCategoryId":null,"ListUrlMain":null,"RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":"","EPubDate":null,"PubModel":null,"JCR":null,"JCRName":null,"Score":null,"Total":0}
Pub Date : 2023-01-01DOI: 10.32604/jrm.2023.027441
{"title":"In Situ Generation of Copper Nanoparticles in Heat-Treated Copper-Containing Masson’s Pine as a Preservative Process for Sawn Timber","authors":"","doi":"10.32604/jrm.2023.027441","DOIUrl":"https://doi.org/10.32604/jrm.2023.027441","url":null,"abstract":"","PeriodicalId":16952,"journal":{"name":"Journal of Renewable Materials","volume":null,"pages":null},"PeriodicalIF":0.0,"publicationDate":"2023-01-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":null,"resultStr":null,"platform":"Semanticscholar","paperid":"69856084","PeriodicalName":null,"FirstCategoryId":null,"ListUrlMain":null,"RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":"","EPubDate":null,"PubModel":null,"JCR":null,"JCRName":null,"Score":null,"Total":0}
Pub Date : 2023-01-01DOI: 10.32604/jrm.2022.021473
C. Gao, Yang Wu, Haibo Xie
{"title":"Fully Bio-Based Composites of Poly (Lactic Acid) Reinforced with Cellulose-Graft-Poly-(ε-Caprolactone) Copolymers","authors":"C. Gao, Yang Wu, Haibo Xie","doi":"10.32604/jrm.2022.021473","DOIUrl":"https://doi.org/10.32604/jrm.2022.021473","url":null,"abstract":"","PeriodicalId":16952,"journal":{"name":"Journal of Renewable Materials","volume":null,"pages":null},"PeriodicalIF":0.0,"publicationDate":"2023-01-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":null,"resultStr":null,"platform":"Semanticscholar","paperid":"69843631","PeriodicalName":null,"FirstCategoryId":null,"ListUrlMain":null,"RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":"","EPubDate":null,"PubModel":null,"JCR":null,"JCRName":null,"Score":null,"Total":0}
Pub Date : 2023-01-01DOI: 10.32604/jrm.2022.023261
Dongfang Huang, P. Lv, C. Zhong, Xingsheng Zhou, Zhichen Liu
{"title":"Study on Hydrogen Storage Properties, Anti-Oxide Ability and Rate Limiting Step of ZrCr-Based Alloy after Introducing Cobalt as Additive","authors":"Dongfang Huang, P. Lv, C. Zhong, Xingsheng Zhou, Zhichen Liu","doi":"10.32604/jrm.2022.023261","DOIUrl":"https://doi.org/10.32604/jrm.2022.023261","url":null,"abstract":"","PeriodicalId":16952,"journal":{"name":"Journal of Renewable Materials","volume":null,"pages":null},"PeriodicalIF":0.0,"publicationDate":"2023-01-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":null,"resultStr":null,"platform":"Semanticscholar","paperid":"69847196","PeriodicalName":null,"FirstCategoryId":null,"ListUrlMain":null,"RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":"","EPubDate":null,"PubModel":null,"JCR":null,"JCRName":null,"Score":null,"Total":0}
Pub Date : 2023-01-01DOI: 10.32604/jrm.2022.023266
Yiguang Wang, Zhe Zhang, Xun Zhang
Fibre can enhance the mechanical properties of cement-based composites, but fibre also degrades their workability. However, the quantitative effects of fiber content and length-diameter ratio on alkali-activated materials are still unclear. Various aspect ratio, volume fraction of polyvinyl alcohol fibre (PVAF), and various water-binder ratio were employed to prepare a total of 26 groups of fibre reinforced alkali-activated composite (FRAAC). The influence of PVAF fibre factor (product of fiber volume fraction and length-diameter ratio) on flowability, compactness, strength, and crack fractal dimension of FRAAC was researched. The influence of water-binder ratio on the plastic viscosity of FRAAC was more significant than that on the yield stress. When fibre factor was lower than critical value of 150, the influence of fibres could be overlooked. The reason was that the space between fibres was distant, so the flowability of FRAAC was not impacted by PVAF. At this time, fibres were challenging to restrict the cracks in matrix and increase their mechanical properties. When fibre factor was higher than critical value 150 and lower than density packing value 450, the flexural strength, compressive strength and crack fractal dimension of FRAAC were considerably enhanced, and the FRAAC could still flow easily under dead weight. When fibre factor were above 450, noteworthy fibre balling considerably decreased the flowability, leading to poor solidity and reduced compressive strength. Hence, the ideal content of PVAF in alkali activated composite is between 150/(l/d) and 450/(l/d).
{"title":"Characteristic of Fresh and Harden Properties of Polyvinyl Alcohol Fibre Reinforced Alkali Activated Composite","authors":"Yiguang Wang, Zhe Zhang, Xun Zhang","doi":"10.32604/jrm.2022.023266","DOIUrl":"https://doi.org/10.32604/jrm.2022.023266","url":null,"abstract":"Fibre can enhance the mechanical properties of cement-based composites, but fibre also degrades their workability. However, the quantitative effects of fiber content and length-diameter ratio on alkali-activated materials are still unclear. Various aspect ratio, volume fraction of polyvinyl alcohol fibre (PVAF), and various water-binder ratio were employed to prepare a total of 26 groups of fibre reinforced alkali-activated composite (FRAAC). The influence of PVAF fibre factor (product of fiber volume fraction and length-diameter ratio) on flowability, compactness, strength, and crack fractal dimension of FRAAC was researched. The influence of water-binder ratio on the plastic viscosity of FRAAC was more significant than that on the yield stress. When fibre factor was lower than critical value of 150, the influence of fibres could be overlooked. The reason was that the space between fibres was distant, so the flowability of FRAAC was not impacted by PVAF. At this time, fibres were challenging to restrict the cracks in matrix and increase their mechanical properties. When fibre factor was higher than critical value 150 and lower than density packing value 450, the flexural strength, compressive strength and crack fractal dimension of FRAAC were considerably enhanced, and the FRAAC could still flow easily under dead weight. When fibre factor were above 450, noteworthy fibre balling considerably decreased the flowability, leading to poor solidity and reduced compressive strength. Hence, the ideal content of PVAF in alkali activated composite is between 150/(l/d) and 450/(l/d).","PeriodicalId":16952,"journal":{"name":"Journal of Renewable Materials","volume":null,"pages":null},"PeriodicalIF":0.0,"publicationDate":"2023-01-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":null,"resultStr":null,"platform":"Semanticscholar","paperid":"69847210","PeriodicalName":null,"FirstCategoryId":null,"ListUrlMain":null,"RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":"","EPubDate":null,"PubModel":null,"JCR":null,"JCRName":null,"Score":null,"Total":0}
Pub Date : 2023-01-01DOI: 10.32604/jrm.2023.023849
Meng-qi Cong, Yang Zhang, Yunlong Zhang, X. Liu, Y. Lu, Xiao-ping Li
{"title":"Tensile Properties and Wear Resistance of Mg Alloy Containing High Si as Implant Materials","authors":"Meng-qi Cong, Yang Zhang, Yunlong Zhang, X. Liu, Y. Lu, Xiao-ping Li","doi":"10.32604/jrm.2023.023849","DOIUrl":"https://doi.org/10.32604/jrm.2023.023849","url":null,"abstract":"","PeriodicalId":16952,"journal":{"name":"Journal of Renewable Materials","volume":null,"pages":null},"PeriodicalIF":0.0,"publicationDate":"2023-01-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":null,"resultStr":null,"platform":"Semanticscholar","paperid":"69850176","PeriodicalName":null,"FirstCategoryId":null,"ListUrlMain":null,"RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":"","EPubDate":null,"PubModel":null,"JCR":null,"JCRName":null,"Score":null,"Total":0}
{"title":"Role of Calcination Temperature on Isosorbide Production from Sorbitol Dehydration over the Catalyst Derived from Ce(IV) Sulfate","authors":"Medta Boupan, Kanyapak Prompang, Achiraya Chompunuch, Piwat Boonma, Arthit Neramittagapong, S. Theerakulpisut, Sutasinee Neramittagapong","doi":"10.32604/jrm.2023.026397","DOIUrl":"https://doi.org/10.32604/jrm.2023.026397","url":null,"abstract":"","PeriodicalId":16952,"journal":{"name":"Journal of Renewable Materials","volume":null,"pages":null},"PeriodicalIF":0.0,"publicationDate":"2023-01-01","publicationTypes":"Journal Article","fieldsOfStudy":null,"isOpenAccess":false,"openAccessPdf":"","citationCount":null,"resultStr":null,"platform":"Semanticscholar","paperid":"69854312","PeriodicalName":null,"FirstCategoryId":null,"ListUrlMain":null,"RegionNum":4,"RegionCategory":"材料科学","ArticlePicture":[],"TitleCN":null,"AbstractTextCN":null,"PMCID":"","EPubDate":null,"PubModel":null,"JCR":null,"JCRName":null,"Score":null,"Total":0}