Journal of Istanbul University Faculty of Dentistry最新文献

Purpose: The purpose of this study was to compare the sealing ability of temporary restorative materials at 24 hrs and 1 week.

Materials and methods: Endodontic access cavities were prepared in 56 extracted lower incisor-teeth and divided into 5 groups (n=10). Standard 5 mm deep access preparations were completed and root canals were prepared to size ISO #30 file. The access cavities were restored as follows: Group 1: temporary restorative material (Ceivitron); Group 2: glass ionomer cement (Fuji II); Group 3: zinc oxide-eugenol cement (IRM); Group 4: zinc phosphate cement (Adhesor); Group 5: polytetrafluoroetylene tape (PTFE). The quality of the coronal sealing of each specimen was measured (24 hrs and 1 week) using fluid transport model. The data was analyzed with repeated measurements ANOVA, Tukey' HSD and Paired samples T-Tests.

Results: A significant difference was found among the groups at all time-periods (p<0.05). At 24 hrs, PTFE showed similar leakage with Ceivitron, IRM, and Fuji II but it showed higher leakage than Adhesor. At 1 week, Ceivitron showed higher leakage than PTFE, meanwhile PTFE showed similar leakage with IRM, Fuji II, and Adhesor (p>0.05). Sealing ability of IRM and PTFE groups significantly increased by time (p<0.05 and p<0.001 respectively).

Conclusion: Within the limitations of this study, PTFE showed an acceptable short-term sealing capability when compared to the other commonly used temporary restorative materials at 1 week measurements.

Purpose: The purpose of the study was to evaluate the postoperative sensitivity of posterior Class I composite restoration at short-term, restorated with two different all-in-one self-etch adhesives with or without surface sealant application.

Materials and methods: 44 restorations were inserted in 11 patients who required Class I restorations in their molars. Each patient received 4 restorations, thus four groups were formed; (1) G-Aenial Bond (GC, Japan); (2) Clearfil S3 Bond (Kuraray, Japan); (3) G-Aenial Bond+Fortify Plus (Bisco, USA), (4) Clearfil S3 Bond+Fortify Plus. Sensitivity was evaluated at 24h, 7, 15, and 30 days using cold air, ice, and pressure stimuli using a visual analog scale. Comparisons of continuous variables between the sensitivity evaluations were performed using the Friedman's One-Way Analysis of Variance with repeated measures test (p<0.05).

Results: The type of adhesive used and the application of a surface sealant had no significant effects in postoperative sensitivity (p>0.05). The use of Clearfil S3 Bond resulted in almost the same level of postoperative sensitivity as did the use of G-Aenial Bond. The highest sensitivity scores were observed for the surface sealant applied teeth without any statistical significance (p>0.05).

Conclusion: Self etch adhesives displayed postoperative sensitivity. The sensitivity scores slightly decreased at the end of 30 days (p>0.05). Surface sealant application did not result in a decrease in sensitivity scores for either dentin adhesives.

Purpose: To assess the shrinkage of Free Gingival Graft (FGG) in horizontal and vertical dimensions and calculate the changes in the surface area of the transplanted tissue in a 3 months period.

Materials and methods: total of 30 FGG were placed aiming to increase attached gingiva around recession sites. Vertical recessions, horizontal recessions, surface area, plaque index, gingival index, periodontal probing depth and clinical attachment level were assesed at baseline, 1 and 3 months postoperatively.

Results: Graft shrinkage between baseline and 1 month was more evident than 1 to 3 months in either dimensions. Both horizontal and vertical dimensions were significantly decreased (p<0.001) at 1 and 3 months post operatively. There was no significant change in PI and GI scores postoperatively compared to baseline (p>0.05).

Conclusion: The shrinkage of vertical and horizontal dimensions of the grafts were almost equal unlike the literature. In addition, the different dimensional changes observed in individual level deserve further research.

Purpose: The aim of the present study was to investigate the prevalence of dental anomalies in a Turkish population according to the gender and age.

Materials and methods: A retrospective study was performed using panoramic radiographs of 2025 patients (885 males and 1140 females) ranging in age from 9 to 35 (mean age 25.61±10.04) years attending Department of Oral Radiology, University of Istanbul, Faculty of Dentistry. These patients were examined to determine the presence of developmental dental anomalies involving hypodontia, hyperdontia, microdontia, taurodontism and other root anomalies. The incidence of these anomalies were assessed according to the gender and age.

Results: Among the 2025 subjects, a total of 96 individuals (42 males and 54 females) showed at least one of the selected dental anomalies (4.74%). Tooth agenesis was the most common dental abnormality (1.77%) followed by taurodontism (1.18%), hyperdontia (0.79%), microdontia (0.54%) and root anomalies (0.44%), respectively.

Conclusion: Tooth agenesis is the most common developmental dental anomaly in the studied Turkish population followed by taurodontism.

Giant cell granuloma is rare in the head and neck region and most commonly affects the maxilla and mandible. Giant cell granulomas are benign but occasionally aggressive lesions that are traditionally treated with surgery. Because it is a benign process, less radical and non-surgical treatment alternatives are required. Corticosteroid injection is a viable alternative in the treatment of central giant cell granuloma to avoid surgery. We aim to present a case which was successfully treated with intralesional corticosteroid injection in the maxilla.

Dens invaginatus is a developmental anomaly resulting from epithelial invagination of the tooth crown before calcification. Endodontic treatment of teeth affected by dens invaginatusmay be difficult and complex due to aberrant anatomy. Combined orthograde and surgical approaches for successful treatment of dens invaginatus are effective. This report describes the successful treatmentand results atthe 12-month follow-up of a maxillary lateral incisor showing dens invaginatus type II, a large periapical lesion and an open apex by using combined surgical and endodontic treatment.

Purpose: To evaluate the effect of hormone replacement therapy(HRT) on periodontal treatment outcomes in a group of postmenopausal women with periodontitis.

Materials and methods: 23 post-menopausal chronic periodontitis patients were included in this study. The test group(n=11) consisted of women who started HRT with this study and received conjugated estrogen and medroxyprogesteron. The control group(n=12) was women not taking any HRT or supplement therapy. Study groups received the same periodontal treatment. All subjects examiend by recording the following: plaque index (PI), sulcus bleeding index (SBI), periodontal pocket depth (PD) and relative attachment level (RAL) from 6 sites in each tooth. Measurements were recorded at the baseline, 1 month, 3 months, and 6 months following periodontal treatment. Serum estrogene level and bone mineral density was recorded at baseline and 6 months following periodontal treatment.

Results: The GI change was greater in the control group. There wasn't significant difference by means of PD, the attachment gain was significantly greater in the HRT receiving group.

Conclusion: HRT seems to have a positive effect on periodontal treatment outcomes.

The International Caries Detection and Assessment System (ICDAS) is a clinical scoring system which allows detection and assessment of caries activity. ICDAS was developed for use in clinical research, clinical practice and for epidemiological purposes. A recent review of caries detection criteria systems found that there were inconsistencies among the research criteria for caries measuring systems. There is a need to an uniform system which allows comparison of data collected in different researches. ICDAS allows detection of caries process at every stage and characterization of the caries activity status of lesion. Later, the criteria were modified and ICDAS II created. The aim of this review is to inform about the ICDAS II and make a comparison between ICDAS II criteria and other caries detection systems.

Purpose: Adequate polymerization is a crucial factor in obtaining optimal physical properties and a satisfying clinical performance from composite resin materials. The aim of this study was to evaluate the polymerization efficiency of dual-cure resin cement cured with two different light curing units under zirconia structures having differing thicknesses.

Materials and methods: 4 zirconia discs framework in 4 mm diameter and in 0.5 mm, 1 mm and 1.5 mm thickness were prepared using computer-aided design system. One of the 0.5 mm-thick substructures was left as mono-layered whereas others were layered with feldspathic porcelain of same thickness and ceramic samples with 4 different thicknesses (0.5, 1, 1.5 and 2.0 mm) were prepared. For each group (n=12) resin cement was light cured in polytetrafluoroethylene molds using Light Emitting Diode (LED) or Quartz-Tungsten Halogen (QHT) light curing units under each of 4 zirconia based discs (n=96). The values of depth of cure (in mm) and the Vickers Hardness Number values (VHN) were evaluated for each specimen.

Results: The use of LED curing unit produced a greater depth of cure compared to QTH under ceramic discs with 0.5 and 1 mm thickness (p<0.05).At 100μm and 300 μm depth, the LED unit produced significantly greater VHN values compared to the QTH unit (p<0.05). At 500 μm depth, the difference between the VHN values of LED and QTH groups were not statistically significant.

Conclusion: Light curing may not result in adequate resin cement polymerization under thick zirconia structures. LED light sources should be preferred over QTH for curing dual-cure resin cements, especially for those under thicker zirconia restorations.

Purpose: This study investigated the influence of sealant application on stain resistance of a nanohybrid resin composite compared to the efficacy of a bonding agent used as a surface sealant on prolonging color stability of the resin composite.

Materials and methods: 28 disc-shaped materials were prepared from a nano-hybrid resin composite Filtek Z550 and assigned to four groups: G1K: nonsealed; G2:Adper Single Bond; G3: Fortify ; G4: Biscover LV. After 24 h storage in distilled water at 37˚C, all specimens were subjected to thermocycling and immersed into coffee solution. Color measurements were performed using spectrophotometer (VITA Easyshade; Vident) according to CIEL*a*b* system.

Results: Color change values were significantly different among the groups in each evaluation period except for after thermocycling (p<0.05). For 7 days evaluation period, the difference between G3 and G4 group was statistically significant while G4 exhibited statistically significant differences (p<0.05 and p<0.0001 respectively) compared to control (G1) in 14 day whereas no significant difference was found between GI and GII in 28-day evaluation period. However, ΔE values of sealed specimens (GIII, GIV) differed significantly from non-sealed (GI) specimens after 28 days of immersion in coffee solution (p<0.05 and p<0.0001 respectively).

Conclusion: It may be concluded that using a bonding agent as a surface sealant does not increase stain resistance of resin composites of the sealants evaluated. Biscover LV showed the highest efficacy to prolong color stability of the resin composite.